Stainless Steel 422 Plates
Table of Content
-
Product Specification
-
Chemical Composition
-
Mechanical Composition
-
Related Products
Stainless Steel 1.4935 Plates, Ss 422 Plates, Astm A240 Ss 422 Plates, Ss 422 2d Finish Plates, Stainless Steel 422 Hot Rolled Plate, Stainless Steel 422 Cold Rolled Plates, Stainless Steel 422 Coils, Stainless Steel S42200 Plates, Stainless Steel 422 Plates Suppliers In Mumbai, India
Ss 422 Hr Plates, Stainless Steel 422 2b Finish Plates, Ss 422 Plates Exporter, Ss 422 Cold Rolled Plates, 422 Stainless Steel Suppliers, Stainless Steel 422 Coil, Stainless Steel 422 Plain Sheets, Ss 422 Ba Finish Sheets, Stainless Steel 422 Sheet Cut Piece, 422 Stainless Steel Circle, Ss 422 Plates Exporter In Mumbai.
DETAILED INFORMATION
As one of the leading Exporters, stockists, and suppliers of ferrous and nonferrous products, Purohit Pipe Industries also deals with household stainless steel products and stainless steel 422 plates. Moreover, we Exporter the entire product according to the customer’s specifications and measurements.
Chemical compositions of stainless steel 422 plates include carbon, manganese, silicon, phosphorus, sulfur, chromium, nickel, molybdenum, vanadium, and tungsten. There are several specifications for these plates, including standards, material grades, lengths, tolerances, finish forms, widths, thicknesses, shapes, sizes, applications, and conditions.
Physical and mechanical properties of these plates include melting point, electrical conductivity, thermal conductivity, elastic modulus, specific heat, hardness, yield strength, tensile strength, elongation, modulus of expansion, grade, and density. Shims, coils, perforated sheets, chequered sheets, strips, flats, blanks, rings, rolls, and foil plates are some of the forms available.
Stainless Steel 422 Plates are sleek and designed with strength, toughness, and hardness from higher temperatures. These sheets and plates can be heat treated at various high temperatures. These sheets and plates are resistant to general corrosion like crevice corrosion, stress cracking corrosion, and pitting corrosion.
Freshwater, steam, alkalis, and polluted environments are not a problem for these plates and sheets. They can provide service up to 1250 degrees Fahrenheit without deformation. These products are resistant to oxidation corrosion and scaling corrosion.
After production from the industry, stainless steel 422 plates undergo many tests, such as flaring, flattening, macro, impact, impact, PMI, hardness, chemical, and mechanical tests, micro tests, radiography tests, and so on.
CITIES WE DELIVER
Adoni, Amaravati, Anantapur, Chandragiri, Chittoor, Dowlaiswaram ,Eluru, Guntur, Kadapa, Kakinada, Kurnool, Machilipatnam, Nagarjunakoṇḍa, Rajahmundry, Srikakulam, Tirupati, Vijayawada, Visakhapatnam, Vizianagaram, Yemmiganur, Itanagar, Dhuburi, Dibrugarh, Dispur, Guwahati, Jorhat, Nagaon, Sivasagar, Silchar, Tezpur, Tinsukia, Ara, Barauni, Begusarai, Bettiah, Bhagalpur, Bihar, Sharif, Bodh Gaya, Buxar, Chapra, Darbhanga, Dehri, Dinapur Nizamat, Gaya, Hajipur, Jamalpur, Katihar, Madhubani, Motihari, Munger, Muzaffarpur, Patna, Purnia, Pusa, Saharsa, Samastipur, Sasaram, Sitamarhi, Siwan, Chandigarh, Ambikapur, Bhilai, Bilaspur, Dhamtari, Durg, Jagdalpur, Raipur, Rajnandgaon, Daman, Diu, Silvassa, Delhi, New Delhi, Madgaon, Panaji, Ahmadabad, Amreli, Bharuch, Bhavnagar, Bhuj, Dwarka, Gandhinagar, Godhra, Jamnagar, Junagadh, Kandla, Khambhat, Kheda, Mahesana, Morbi, Nadiad, Navsari, Okha, Palanpur, Patan, Porbandar, Rajkot, Surat, Surendranagar, Valsad, Veraval, Ambala, Bhiwani, Chandigarh, Faridabad, Firozpur Jhirka, Gurugram, Hansi, Hisar, Jind, Kaithal, Karnal, Kurukshetra, Panipat, Pehowa, Rewari, Rohtak, Sirsa, Sonipat, Bilaspur, Chamba, Dalhousie, Dharmshala, Hamirpur, Kangra, Kullu, Mandi, Nahan, Shimla, Una, Anantnag, Baramula, Doda, Gulmarg, Jammu, Kathua, Punch, Rajouri, Srinagar, Udhampur, Bokaro, Chaibasa, Deoghar, Dhanbad, Dumka, Giridih, Hazaribag, Jamshedpur, Jharia, Rajmahal, Ranchi, Saraikela, Badami, Ballari, Bengaluru, Belagavi, Bhadravati, Bidar, Chikkamagaluru, Chitradurga, Davangere, Halebid, Hassan, Hubballi-Dharwad, Kalaburagi, Kolar, Madikeri, Mandya, Mangaluru, Mysuru, Raichur, Shivamogga, Shravanabelagola, Shrirangapattana, Tumakuru, Vijayapura, Alappuzha, Vatakara, Idukki, Kannur, Kochi, Kollam, Kottayam, Kozhikode, Mattancheri, Palakkad, Thalassery, Thiruvananthapuram, Thrissur, Kargil, Leh, Balaghat, Barwani, Betul, Bharhut, Bhind, Bhojpur, Bhopal, Burhanpur, Chhatarpur, Chhindwara, Damoh, Datia, Dewas, Dhar, Dr. Ambedkar Nagar (Mhow), Guna, Gwalior, Hoshangabad, Indore, Itarsi, Jabalpur, Jhabua, Khajuraho, Khandwa, Khargone, Maheshwar, Mandla, Mandsaur, Morena, Murwara, Narsimhapur, Narsinghgarh, Narwar, Neemuch, Nowgong, Orchha, Panna, Raisen, Rajgarh, Ratlam, Rewa, Sagar, Sarangpur, Satna, Sehore, Seoni, Shahdol, Shajapur, Sheopur, Shivpuri, Ujjain, Vidisha, Ahmadnagar, Akola, Amravati, Aurangabad, Bhandara, Bhusawal, Bid, Buldhana, Chandrapur, Daulatabad, Dhule, Jalgaon, Kalyan, Karli, Kolhapur, Mahabaleshwar, Malegaon, Matheran, Mumbai, Nagpur, Nanded, Nashik, Osmanabad, Pandharpur, Parbhani, Pune, Ratnagiri, Sangli, Satara, Sevagram, Solapur, Thane, Ulhasnagar,n Vasai-Virar, Wardha, Yavatmal, Imphal, Cherrapunji, Shillong, Aizawl, Lunglei, Kohima, Mon, Phek, Wokha, Zunheboto, Balangir, Baleshwar, Baripada, Bhubaneshwar, Brahmapur, Cuttack, Dhenkanal, Kendujhar, Konark, Koraput, Paradip, Phulabani, Puri, Sambalpur, Udayagiri, Karaikal, Mahe, Puducherry, Yanam, Amritsar, Batala, Chandigarh, Faridkot, Firozpur, Gurdaspur, Hoshiarpur, Jalandhar, Kapurthala, Ludhiana, Nabha, Patiala, Rupnagar, Sangrur, Abu, Ajmer, Alwar, Amer, Barmer, Beawar, Bharatpur, Bhilwara, Bikaner, Bundi, Chittaurgarh, Churu, Dhaulpur, Dungarpur, Ganganagar, Hanumangarh, Jaipur, Jaisalmer, Jalor, Jhalawar, Jhunjhunu, Jodhpur, Kishangarh, Kota, Merta, Nagaur, Nathdwara, Pali, Phalodi, Pushkar, Sawai Madhopur, Shahpura, Sikar, Sirohi, Tonk, Udaipur, Gangtok, Gyalshing, Lachung, Mangan, Arcot, Chengalpattu, Chennai, Chidambaram, Coimbatore, Cuddalore, Dharmapuri, Dindigul, Erode, Kanchipuram, Kanniyakumari, Kodaikanal, Kumbakonam, Madurai, Mamallapuram, Nagappattinam, Nagercoil, Palayamkottai, Pudukkottai, Rajapalayam, Ramanathapuram, Salem, Thanjavur, Tiruchchirappalli, Tirunelveli, Tiruppur, Thoothukudi, Udhagamandalam, Vellore, Hyderabad, Karimnagar, Khammam, Mahbubnagar, Nizamabad, Sangareddi, Warangal, Agartala, Agra, Aligarh, Amroha, Ayodhya, Azamgarh, Bahraich, Ballia, Banda, Bara Banki, Bareilly, Basti, Bijnor, Bithur, Budaun, Bulandshahr, Deoria, Etah, Etawah, Faizabad, Farrukhabad-cum-Fatehgarh, Fatehpur, Fatehpur Sikri, Ghaziabad, Ghazipur, Gonda, Gorakhpur, Hamirpur, Hardoi, Hathras, Jalaun, Jaunpur, Jhansi, Kannauj, Kanpur, Lakhimpur, Lalitpur, Lucknow, Mainpuri, Mathura, Meerut, Mirzapur-Vindhyachal, Moradabad, Muzaffarnagar, Partapgarh, Pilibhit, Prayagraj, Rae Bareli, Rampur, Saharanpur, Sambhal, Shahjahanpur, Sitapur, Sultanpur, Tehri, Varanasi, Almora, Dehra Dun, Haridwar, Mussoorie, Nainital, Pithoragarh, Alipore, Alipur Duar, Asansol, Baharampur, Bally, Balurghat, Bankura, Baranagar, Barasat, Barrackpore, Basirhat, Bhatpara, Bishnupur, Budge Budge, Burdwan, Chandernagore, Darjeeling, Diamond Harbour, Dum Dum, Durgapur, Halisahar, Haora, Hugli, Ingraj Bazar, Jalpaiguri, Kalimpong, Kamarhati, Kanchrapara, Kharagpur, Cooch Behar, Kolkata, Krishnanagar, Malda, Midnapore, Murshidabad, Nabadwip, Palashi, Panihati, Purulia, Raiganj, Santipur, Shantiniketan, Shrirampur, Siliguri, Siuri, Tamluk, Titagarh
ASTM A240 SS 422 Plate Specifications
Description | ASTM A240 / ASME SA240 Stainless Steel Plates, ASTM A240 Hot Rolled Stainless Steel Plates |
Standard | ASTM, ASME, BS, DIN, EN |
Material | 310S, 310, 309, 309S, 316, 316L, 316Ti, 317, 317L, 321, 321H, 347, 347H, 304, 304L, |
302, 301, 201, 202, 403, 405, 409, 409L, 410, 410S, 420, 430, 631, 904L, Duplex, etc | |
Specification |
Cold rolled: 1219mm * 2438mm (4′ x 8′), 1219mm * 3048mm (4′ x 10′), 1220mm * 2440mm, 1250mm * 2500mm or as your requirement. Hot rolled: 1500mm * 2000mm, 1000mm * 3000mm, 1500mm * 4000mm, 1500m * 6000mm or as your requirement. |
Technique | Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
Form | Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Etc. |
Surface | 2B, 2D, BA, NO. 1, NO. 4, NO.8, 8K, Mirror, Checkered, Embossed, Hair Line, Sand Blast, Brush, Etching |
Thickness | 0.25-200mm, 0.3mm to 120mm |
Width | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm |
Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, 12000mm |
Package | As required, or the standard export seaworthy package. |
Value Added Services | Cladding, Heat Treatment, Annealed, Pickling, Polish, Rolling, Cutting, Bending, Forging, Minor Fabrication Etc. |
MTC | The mill test certificate is available in accordance with EN 102043.1 |
ASTM A240 Stainless Steel 422 Chemical Composition
Element |
Content (%) |
Iron, Fe |
~ 82 |
Chromium, Cr |
11.0-13.0 |
Manganese, Mn |
1.00 |
Nickel, Ni |
0.5-1.0 |
Molybdenum, Mo |
0.75-1.25 |
Tungsten, W |
0.75-1.25 |
Silicon, Si |
0.75 |
Carbon, C |
0.20-0.25 |
Vanadium, V |
0.15-0.3 |
Phosphorous, P |
0.025 |
Sulfur, S |
0.025 |
ASTM A240 Stainless Steel 422 Mechanical Properties
Properties |
Metric |
Imperial |
Elastic modulus |
190-210 GPa |
27557–30458 ksi |
Poisson’s ratio |
0.27-0.30 |
0.27-0.30 |
ASTM A240 TP422 Stainless Steel Plate Physical Properties
Density (lb / cu. in.) |
0.287 |
Specific Gravity |
7.94 |
Specific Heat (Btu/lb/Deg F – [32-212 Deg F]) |
0.12 |
Electrical Resistivity (microhm-cm (at 68 Deg F)) |
432 |
Melting Point (Deg F) |
2590 |
Modulus of Elasticity Tension |
28 |
ASTM A240 TP 422 Equivalent
STANDARD |
WERKSTOFF NR. |
UNS |
SS 422 |
1.4935 |
S42200 |
SS 422 Plate Sizes
Sizes in mm |
Availability |
0.4 |
√ |
0.5 |
√ |
0.8 |
√ |
1 |
√ |
1.2 |
√ |
1.6 |
√ |
2 |
√ |
3 |
√ |
4 |
√ |
5 |
√ |
6 |
√ |
8 |
√ |
10 |
√ |
12 |
√ |
16 |
√ |
20 |
√ |
25 |
√ |
422 Stainless Steel Plate Gauges
Nominal Decimal |
Standard Variance From |
|
Metal Gauge |
(Approximate Inches) |
Nominal Decimal (+/- Inches) |
7 |
0.1793 |
0.0080 |
8 |
0.1644 |
0.0080 |
9 |
0.1495 |
0.0080 |
10 |
0.1345 |
0.0070 |
11 |
0.1196 |
0.0050 |
12 |
0.1046 |
0.0050 |
13 |
0.0897 |
0.0050 |
14 |
0.0747 |
0.0040 |
15 |
0.0673 |
0.0040 |
16 |
0.0598 |
0.0030 |
17 |
0.0538 |
0.0030 |
18 |
0.0478 |
0.0030 |
19 |
0.0418 |
0.0030 |
20 |
0.0359 |
0.0030 |
21 |
0.0329 |
0.0025 |
22 |
0.0299 |
0.0020 |
23 |
0.0269 |
0.0020 |
24 |
0.0239 |
0.0020 |
25 |
0.0209 |
0.0015 |
26 |
0.0179 |
0.0015 |
28 |
0.0149 |
0.0010 |
Types Of Stainless Steel 422 Plate
Stainless Steel 422 Hot Rolled Sheet
ASTM A240 SS 422 Hot Rolled Sheet, ASME SA240 Stainless Steel 422 HR Sheets, UNS S42200 Hot Rolled Sheets, 1.4935 Hot Rolled Sheets, SS 422 Hot Rolled Sheet Exporter, Austenitic Stainless Steel 422 HR Plain Sheet Supplier, SS 422 2B Finish HR Sheets, Stainless Steel 422 BA Finish HR Sheets, Jindal make SS 422 HR Sheets, Stainless Steel 422 Hot Rolled Sheets Exporter in Mumbai/India.
Stainless Steel 422 Cold Rolled Sheet
ASTM A240 SS 422 Cold Rolled Sheet, ASME SA240 Stainless Steel 422 CR Sheets, UNS S42200 Cold Rolled Sheets, 1.4935 Cold Rolled Sheets, SS 422 Cold Rolled Sheet Exporter, Austenitic Stainless Steel 422 CR Plain Sheet Supplier, Stainless Steel 422 2B Finish CR Sheets, SS 422 BA Finish CR Sheets, Jindal make SS 422 CR Sheets, Stainless Steel 422 Cold Rolled Sheets Exporterer in Mumbai/India.
Stainless Steel 422 Hot Rolled Plate
ASTM A240 SS 422 Hot Rolled Plate, ASME SA240 Stainless Steel 422 HR Plates, UNS S42200 Hot Rolled Plates, 1.4935 Hot Rolled Plates, SS 422 Hot Rolled Plate Exporter, Austenitic Stainless Steel 422 HR Plain Plate Supplier, SS 422 2B Finish HR Plates, Stainless Steel 422 BA Finish HR Plates, Jindal make SS 422 HR Plates, Stainless Steel 422 Hot Rolled Plates Exporter in Mumbai/India.
Stainless Steel 422 Cold Rolled Plate
ASTM A240 SS 422 Cold Rolled Plate, ASME SA240 Stainless Steel 422 CR Plates, UNS S42200 Cold Rolled Plates, 1.4935 Cold Rolled Plates, SS 422 Cold Rolled Plate Exporter, Austenitic Stainless Steel 422 CR Plain Plate Supplier, SS 422 2B Finish CR Plates, Stainless Steel 422 BA Finish CR Plates, Jindal make SS 422 CR Plates, Stainless Steel 422 Cold Rolled Plates Exporterer in Mumbai/India.
Stainless Steel 422 Coils
ASTM A240 SS 422 Coils, UNS S42200 Coils, 1.4935 Coils, ASME SA240 Stainless Steel 422 Coils, Stainless Steel 422 Hot Rolled Coils Supplier,SS 422 Coils Exporter, Austenitic Stainless Steel 422 HR Coils, SS 422 CR Coils, Stainless Steel 422 Rings, Jindal make SS 422 Coils, Stainless Steel 422 Coil Exporterer in Mumbai/India.
General Characteristics Of Stainless 422
422 stainless steel is a hardenable steel with a benefit temperature of 1200oF (650oC) and is prepared for warm treatment to attain high mechanical properties.
Utilizations OF STAINLESS 422
A variety of cutting edges and basins were used in compressors and steam turbines, and high-temperature shooting, compressor, turbine wheels, valves, and valve trim were also Exporter.
Producing STAINLESS 422
Large segments should be heated to 1200/1400 degrees Fahrenheit (650/760 degrees Celsius), then cooled to 1900/2150 degrees Fahrenheit (1040/1175 degrees Celsius). After reaching room temperature, forgings should be moderately cooled and toughened or tempered as soon as possible.
Tempering
After heating to 1350/1430oF (730/780oC) and soaking it for four hours, the hardness will be Rc21-25 and the microstructure will be tempered martensite. The isothermal strengthening process involves heating to 1900°F (1040°C), cooling to 1275°F (690°C) for 24 to 48 hours, and cooling by air. In addition to carbide, this treatment will give a hardness of Rb 90-95. A part should be re-solidified after ISO strengthening (1040/1065oC) and tempered to achieve the required mechanical properties.
Solidifying
After heating to 1900oF (1040oC), the douse and oil extinguish to a hardness of Rc45/50. Multifaceted shapes may be marquenched at 650oF (340oC) and air-cooled. Air cooling parts to Ms and extinguishing them will probably cause splitting. Parts should be cooled to room temperature before treatment. As a result of treatment, parts have to be finished to martensite in order to counteract non-uniformities and hardness.
Hardening
Hardening temperatures require past experience in order to determine which temperature is required to achieve desired mechanical properties. It is preferable to harden parts after their solidification when they reach room temperature.
Machinability
Compounds are immediately machined under toughened conditions: they are machined as stainless steel 420.
Weldability
This compound is difficult to weld because of breakage. Preheating is recommended along with a post-weld push to alleviate the welded zones for 4 hours at 1100/1400 degrees Fahrenheit (590/760 degrees Celsius).
Application Industries
- Constructing
- Building bridges
- Industry of Petrochemicals
- Construction of ships
- Engineering
- Purposes of General Structural Design
- Services both offshore and onshore
420 Stainless Steel Plate Packaging
-
We ensure that our products are packed, stored, and transported compliant with international regulations. We pay attention to even the smallest details when it comes to the quality of our products.
All shipping documentation for 420 Stainless Steel Plate delivery from the mill to the customer is provided. Each order is packaged according to the client’s standards, including preparation for export, such as wooden cases or pallets.
In order to move from India, one of our experienced sales representatives evaluates the volume and weight of the belongings and informs the client about packing requirements and various documentation requirements.
420 Stainless Steel Plate Supply Area :
-
In addition to Indonesia, Malaysia, Singapore, Saudi Arabia, Qatar, UAE, Iran, Iraq, Oman, South Africa, Nigeria, Kenya, Italy, UK, we export most of our 420 Stainless Steel Plates every year.
420 Stainless Steel Plate Marking
- 420 Stainless Steel Plate is packaged in such a way that it does not get damaged while in transit. Trademarks (Company’s Logo), Grade, Size, and Lot No are all stamped on all 420 Stainless Steel Plates. Export packaging is in wooden boxes or cases for export. Upon request, custom marking can be done.
420 Stainless Steel Plate Test Certificates
- There should be an Exporter’s test certificate according to EN 10204-3.1 and EN 10204-3.2, as well as a raw materials certificate, a NABL lab report, a radiography report, and a third-party inspection report.
Talk With Experts
Or Send a Message
+919769256593
Distribution Network

Our Product
Our Latest Blogs
The Difference Between Forged Flanges and Cast Flanges
We have talked commonly about forged steel flanges, forged tube, what is forged metal, casting flange, what causes cast, casting porosity, cast trunion, but today lets understand the difference between forged and cast along with the advantages and disadvantages of...
Request A Quote
Fill all information details to consult with us to get services from us
What are our quality inspection standards?
Our key qualities and services comprise of:
• Quality assured goods
• Multiple payment modes
• Experienced crew
• Prompt shipment
• Ethical business policies
• Wide distribution network
Which certifications have we acquired?
Lakshya International has the following certification:
• MSME UDHAYM NO
• GST CERTIFICATE
• CERTIFICATE OF INCORPORATION
• CERTIFICATE OF IMPORT EXPORT CODE
• ISO CERTIFICATE
• PED CERTIFICATE
• CE CERTIFICATE
• MANUFACTURING CERTIFICATE